Description:
Endless flattened zero halogen heat shrink polyolefin tubing with ideal properties for identification by thermal transfer printing. Developed for general purpose and for applications in underground, railway, marine and offshore.
Features:
- Excellent print quality
- Zero halogen
- Ready to use for thermal transfer printers
- Vehicle category Ia according BS6853 (1999)
- 2:1 shrink ratio in inch size
- Shrink temperature > 90°C
- Operating temperature -55°C to +105°C
Ribbons recommended: best print results are achieved with our recommended ribbons
Download:
Standard packaging:
Reels
Size [inch] | Size [mm] | Flat width [nominal value, mm] | Maximum Inside Diameter Recovered [ mm] | Wall Thickness Recovered [nominal value, mm] |
---|---|---|---|---|
3/32 | 2,4 | 4,2 | 1,2 | 0,51 |
1/8 | 3,2 | 5,6 | 1,6 | 0,63 |
3/16 | 4,8 | 7,6 | 2,4 | 0,63 |
1/4 | 6,4 | 10,7 | 3,2 | 0,72 |
3/8 | 9,5 | 15,1 | 4,8 | 0,70 |
1/2 | 12,7 | 20,9 | 6,4 | 0,70 |
3/4 | 19,1 | 30,9 | 9,5 | 0,77 |
1 | 25,4 | 40,5 | 12,7 | 0,92 |
1 1/2 | 38,1 | 60,5 | 19,1 | 0,97 |
2 | 50,8 | 79,3 | 25,4 | 0,97 |
Property | Test method | Typical value |
---|---|---|
Tensile strength | ASTM D 638 | 10 N/mm2 |
Elongation at break | ASTM D 638 | 200% |
Longitudinal change | ASTM D 2671 | -10% to +5% |
Water absorption | ASTM D 570 | ≤ 0,15% |
Specific gravity | ASTM D 792 | 1,40 |
Property | Test method | Typical value |
---|---|---|
Heat shock 4 hours at 175°C | ASTM D 2671 | no dripping, cracking or flowing |
Heat aging 168 hours at 150°C | ASTM D 638 | elongation ≥ 100% |
Low temp. flexibility at -55°C | ASTM D 2671 C | no break, no crack, no detachment of coating or detamination |
Flammability | ASTM D 635-HB | pass |
Optical density of smoke (Dm) | ASTM E 662 | flaming mode 41 non-flaming mode 111 |
Property | Test method | Typical value |
---|---|---|
Dielectric strength | ASTM D 2671 | 20kV/mm |
Volume resistivity | ASTM D 257 | 1014 ohm/cm |
Property | Test method | Typical value |
---|---|---|
Chemical resistance | AMS-DTL-23053/5 | good |
Copper corrosion | ASTM D 2671 B | no corrosion |
Oxygen index | EN ISO 4589-2 (1999) | 36% |
Property | Test method | Typical value |
---|---|---|
Adherence test (eraser method) | SAE AS81531 | legible |
Fluid resistance | MIL-STD-202G method 215K | |
Isopropyl Alcohol \ Mineral spirits blend | 10 rubs (X3) | legible |
Terpene defluxer | 10 rubs (X3) | legible |
H2O \ PGME \ Monoethanolamine | 10 rubs (X3) | legible |
Property | Tape Y201P | Tape Y501P |
---|---|---|
Smear resistance (10 rubs) | ||
Diesel | 3 | 2 |
Hydraulic oil | 1 | 1 |
Unleaded gasoline | 5 | 4 |
Ethyl alcohol 92% | 1 | 1 |
Ethyl alcohol 95% | 1 | 1 |
Legend: | ||
1 - no effect, 2 - slight fading, 3 - moderate fading but still legible, 4 - severe fading and print illegible, 5 - complete print removal |
Property | Test method | Tape Y201P | Tape Y501P |
---|---|---|---|
Scratch test (rough sponge method) | in-house | ||
10 rubs | good | very good | |
Solvent test | in-house | ||
Isopropyl alcohol 99,9% | 10 rubs | good | excellent |
Isopropyl alcohol 99,9% | 20 rubs | good | excellent |
Norms:
- SAE AS81531 4.6.2 *
- MIL-STD-202G method 215K *
- ASTM D 635-HB flammability resistance
- Boeing BS 7239 toxic gas generation M7
Railway normative:
- BS6853 (1999) ehicle category Ia
- EN 45545-2 class HL3
- LUL 1-085: A3 compliant
* when used in conjuction with Y201P or Y501P ribbon